1
The Metallography and Heat Treatment of Iron and Steel
On the contrary it seems probable that a large number of the steels tested were in
a sorbitic rather than in a pearlitic condition because of relatively quick cooling
through the critical range as explained in a subsequent chapter. And while it ...
2
Bulletins of the Engineering Experiment Station, University ...
10, 0.49 Carbon, Sorbitic. Tensile Stress of 55 2(X> lb. per sq. in. applied 20
times Steel No. 10, 0.49 Carbon, Sorbitic. Tensile Stress of 55 200 lb. per sq. in.
applied 20 times: specimen then boiled one hour 379 900 095 200 1 122 400
473 ...
Intricate Spun-Sorbitic Castings Produced in Great Britain by New Process —
Have High Strength, Machinability and Wear Resistance — Useful for Engine
Cylinders and Pistons of All Kinds BY J. E. HURST* Smaller Use of Pig Iron in ...
80,600 0.37 carbon sorbitic—Trentment B. . . . 1.20 carbon normalized . . . . . . . . . .
. . ..'.' ss.aoo Table iv Results Of Compression and TOISIOH TCSIS r——————
Compression Proportional. definite number of reversals of stress will not cause ...
5
Minutes of Proceedings of the Institution of Civil Engineers
A length of ordinary medium-manganese untreated steel was put in, a length of
ordinary sorbitic steel next to it, and a length of the regulated sorbitic steel next to
that. At the end of 10 weeks, the ordinary medium- manganese untreated steel ...
Institution of Civil Engineers (Great Britain), 1935
6
Iron and Steel Magazine
have formed a correct idea of the nature of Sorbitic Steel. The production of this
steel, however, has been described by many technical papers in such a way as
to create the impression that a new steel had been discovered, or, at least, a new
...
7
Transactions of the American Society for Steel Treating
... 30,000 57,700 40.8 63.2 0.37 carbon normalized 34,500 34,900 71,900 29.4
53.5 0.37 carbon sorbitic— Treatment A 80,600 87,300 102,600 23.3 65.1 0.37
carbon sorbitic— Treatment B 61,500 63,100 94,200 25.0 63.0 0.49 carbon
sorbitic ...
American Society for Steel Treating, 1922
34,500 34,900 71,900 29.4 53.5 33.000 0.37 carbon sorbitic-Treatment 80,600
87,300 102,600 23.3 65.1 57,000 0.37 carbon sorbitic-Treatment B 61,500
63,100 94,200 25.0 63.0 45,000 0.49 carbon sorbitic 67,700 69,700 96,900 23.5
57.8 ...
American Society for Metals, 1921
9
The collected works of Sir Humphry Davy ...: Discourses ...
0.37 carbon Sorbitic — Treatment A 82,000 80.600 87,300 102,600 23.3 4. 0.37
Carbon Sorbitic— Treatment B 60,300 61,500 63,100 94,200 25.0 40. 0.49
Carbon Sorbitic 67.300 67,700 69,700 96,900 23.5 3. 0.52 Carbon Normalized
47.200 ...
Sir Humphry Davy, John Davy, 1921
10
Engineering and Contracting
60.300 61.500 63.100 94.200 25.0 63.0 45.000 10.0.49 Carbon sorbitic . . . . . . . . .
.. 67.300 67.700 69.700 96.900 23.5 57.8 48.000 3.0.52 Carbon Normalized
47.200 45.400 47.600 98.000 24.4 41.7 42.000 3. 052 Carbon Sorbitic 79.400 ...